Technical Specification
Product Information | |
Colour | Selected range |
Finish | Semi Glossy |
Mixing Ratio | Base : Hardner |
2 : 1 (By Weight/Volume) | |
Recommended dry film thickness | 200 - 500 microns per |
Theoretical Spreading Rate | 3 â 5 Sq.metre per litre |
Interval before Over coating | Minimum â 16 hours |
Maximum â 48 hours |
Surface Preparation
Steel Surfaces:
Thoroughly Clean All Loose Particles, Chalking Etc.Degrease And Blast Clean To Sa 2 ½ Grade Minimum Of Swedish Specification Sis - 05 - 5900 - 1967.
Concrete Surfaces:
Remove All Dirt Particles, Chalking, Greese Etc By Thorough Wire Bushing. Acid Etching Is Recommended Provided The Residual Acid Can Be Thoroughly Cleaned Out By Water Hosing In High Pressure. Prior To Application Of Metoxy 5150 Ensure That Surface Is Perfectly Clean And Dry And Ambient Temperature Is More Than 5ºc.
Details:
In case the stipulated over coating period is over, for application of subsequent coat of paint the surface should be mildly rubbed with water paper no.100 for better results.
Storage Life :
Up to 12 months in sealed condition.
Dry Heat Resistance: Up to 75º C
Application Details
Method Of Application:
By Brush/ Roller/ Plural Feed Airless Gun.
Product Not Designed For Dip Application.
Pot Life: .5 To 1 Hour.
Thinner / Cleaner: Thinner No.9
System Selection Guide
Surface | 1st Coat | 2nd coat | 3 rd coat | 4 th coat |
Steel | Metoxy5040 Zinc Phosphate Primer | Metoxy 5252 solventless epoxy Coating. | Metoxy 5252 solventless epoxy Coating. |
|
Concrete Surface | Metoxy5070 Epoxy Primer | Metoxy 5252 solventless epoxy Coating. | Metoxy 5252 solventless epoxy Coating. |
|
Chemical Resistance Guide
Exposure | Splash & Spillage | Fumes & Outdoor Exposure |
Acids | Excellent | Excellent |
Alkalis | Excellent | Excellent |
Solvents | Excellent | Excellent |
Salt water | Excellent | Excellent |
![]() |